CERO WOOD
CERO WOOD is a material that implements environmentally friendly recycling and sustainable management.
We are different from traditional WPC manufacturers, focusing on providing services for new materials.
▶▶ Better "wood" than natural wood
Really protect forests and reduce the burden on the earth
Product composition
CERO WOOD is different from the common imitation wood, traditional plastic wood and other materials on the market.
- It can be 100% recycled, and the raw materials can be new materials or recycled materials.
- Micro-foaming technology: strengthen the physical properties of the product
- Bubbles in the material: energy saving through air insulation
- No fiber is added, such as wood flour
- High UV resistance, weather resistant
- Excellent acid, alkali, insulation, water and chemical resistance
- CERO WOOD is more suitable for hot and humid tropical and subtropical environments.
Material characteristics table
CERO WOOD is a micro-foamed lightweight material that is lighter and stronger than wood.
Hardness
Softening temperature(℃)
Item
Method
Result
Description
Density
(g/cm3)
ASTM
D792-13A
0.65
(Type D/1 sec)
ASTM
D2240-15
76
Material properties and strength greater than solid wood.
Bending strength
(kgf/cm2)
ASTM
D790-15A
271
Compressive strength
(kgf/cm2)
ASTM
D695-15
401
Tensile strength
(kgf/cm2)
ASTM
D638-14
212
Shear strength
(kgf/cm2)
ASTM
D732-10
144
Impact strength
(kJ/m2)
ASTM
D256-10
1.33
Coefficient of friction
ASTM
D1894-14
0.52
If the value is above 0.45, there will be a non-slip effect.
Nail force
ASTM
D1037-12
339
The bite force of the material on the nail.
The higher the value, the tighter the bite.
(10N，Heating rate 50℃/h)
ASTM
D1525-09
100
Deformation resistant to nearly 100°C
Resistance to cold and heat cycles
(10 cycle，-40℃, 4h~70℃, 4h)
ASTM
D2247-15
No abnormal appearance
Suitable for cold or tropical areas
Water absorption(%)
CNS
9907
0.18
Almost no water absorption, no mold
Water absorption length change rate(%)
CNS
9907
0.08
CERO WOOD does not absorb water, and the length change rate after water absorption is extremely low.
Elongation rate(%)
ASTM
D638-14
1.2
The material is ductile, which effectively avoids brittle cracking of the material.
Heavy metal content (ppm)
Pb
EN71-3
：1994
N.D.
Sb
N.D.
As
N.D.
Ba
N.D.
Cd
N.D.
Cr
N.D.
Hg
N.D.
Se
N.D.
Comparison Chart
|
Item \ Material |
CERO WOOD |
Solid Wood |
WPC |
|
High Rigidity |
● |
○ |
▲ |
|
High Toughness |
● |
○ |
▲ |
|
Non-slip |
● |
○ |
▲ |
|
Non-toxic |
● |
○ |
▲ |
|
UV Resistance |
● |
○ |
▲ |
|
Low Water Absorption |
● |
▲ |
○ |
|
Pest Control, Anti-mildew |
● |
▲ |
○ |
|
Low Expansion And Shrinkage |
● |
▲ |
○ |
|
Renewable |
● |
▲ |
○ |
|
No Deformation |
● |
▲ |
○ |
|
No Crack |
● |
▲ |
○ |
●Good ○General ▲Poor
Common comparison
CERO WOOD uses PS material, and other products on the market commonly use PP and PE materials, both of which are environmentally friendly materials.
-
PP and PE materials are lighter and have a price advantage.
However, PP and PE materials have poor sunlight resistance and are prone to embrittlement, resulting in problems such as cracks and warpage. -
PS material has high rigidity and hardness, but is heavy and brittle.
CERO WOOD solves this problem through special formulation and micro-foaming technology, while maintaining the high rigidity and hardness of PS material, which is very suitable for structural panels. - PS material also has excellent UV resistance and is suitable for outdoor applications.
We believe that every material is suitable for use.
In long-term use, CERO WOOD has overcome the problems encountered by ordinary sheets with its material expertise.
We enhance product value and give customers better choices.
SGS test report
- Tested by SGS, free of formaldehyde and six heavy metals
CERO WOOD application
- Suitable for indoor and outdoor panels, outdoor plank roads, furniture, kitchen utensils, system cabinets, various building panels, etc.